Durability of concrete made with recycled concrete aggregates after exposure to elevated temperatures

Résumé

The behaviour of concrete made with recycled concrete aggregates (RCA) at room temperature is well-studied. However, some points still need to be addressed, especially in extreme conditions such as durability and high temperature. This paper evaluates the effect of elevated temperatures on the durability of concrete made with RCA. Three concrete mixes were studied: concrete with NA (reference), 100 % direct replacement (DR) mix (RCA-100-DR) and 100 % strength-based replacement (SBR) mix (RCA-100-SBR). The latter was designed to achieve the same performance as concrete made with NA. Mixes were exposed to temperatures of 200 • C, 400 • C and 600 • C. After cooling, durability-loss due to thermal exposure was evaluated through water porosity, capillary water absorption, permeability, chloride diffusion and accelerated carbonation tests. At room temperature, the direct addition of RCA decreased all durability parameters. The SBR mix recovered some of the durability properties. Exposure to high temperatures decreases all the properties, but it varies depending on the property. The concrete made with NA and the SBR mix showed similar performance. The durability was also evaluated using a performance-based approach, both at

Domaines

Génie civil
Fichier principal
Vignette du fichier
Durability_M_S_Diff.pdf (2.5 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04007416 , version 1 (28-02-2023)

Identifiants

Citer

Bruno Fernandes, Michel Khodeir, Céline Perlot-Bascoules, Hélène Carré, Jean-Christophe Mindeguia, et al.. Durability of concrete made with recycled concrete aggregates after exposure to elevated temperatures. Materials and structures, 2023, 56 (1), pp.25. ⟨10.1617/s11527-023-02111-1⟩. ⟨hal-04007416⟩
38 Consultations
76 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More